>YAMAKIN CO., LTD.

ZEOQUICK

Firing Program (ZEO CE LIGHT & ZEOQUICK)

item/type	Drying time (Min.)	Start Temp. (℃)	Heat Rate (°C/Min.)	Firing Temp. (℃)	Hold Time (Min.)	Vacuum Rate (kPa)<cmHg>
Opaque*1	5-10	450-500	60	920	1	97<73>
Margin*2	6-9	550-600		900
Dentine etc*3
Additional Dentine Firing
Glaze (Self Glaze)	4			880		Atmosphere
Supplement	6			790-830*4		97<73>
Stain (Inner)	4			820		97<73>
Stain (Surface)	4			880		Atmosphere

Recommended Firing Program for Ni-Cr or Co-Cr alloys

Ni-Cr alloys basically have low thermal conductivity. So, a longer Hold Time is recommended to avoid insufficient firing (unbaked). This procedure allows porcelain to maintain sufficient strength and will prevent cracks even when tensile stresses are put on the porcelain. Therefore, we recommend the following firing program. These firing instructions are strongly recommended, especially for dental implant cases where the metal volume is large.

	Drying time (Min.)	Start Temp. (℃)	Vacuum	Heat rate (°C/Min.)	Firing temp. (℃)	Hold time (min: air)
Opaque*1	5-10	450-500	○	60	940	2-3
Dentine*3	6-9	550-600	○	60	920	2-3

*1 Super Opaque, Shade Opaque
*2 Margin
*3 Opaque Dentine, Dentine, Enamel, Opal Enamel, Translucent, Accent, Gum
*4 Fire at lower temperature if gloss is not preferable. Fire at higher temperature if gloss is preferable
(Note) Depending on the firing conditions, there may be cases where the original properties are not demonstrated. Please confirm the points below for use.
･Conditions of firing differ depending on types or shapes of furnaces. Adjust the temperature in the range of ±20℃.
･Appropriate condition of Opaque after firing is slightly glossy, and appropriate condition of Dentine after firing is a light gloss.

Warning for Users
YAMAKIN CO., LTD. assumes no responsibility whatsoever for any direct or indirect damage, loss, prejudice or emotional distress caused by wrong usage of our products, such as mixture with other-brand products or failure to follow the instructions provided in our manual.