Achieve both high translucency and high strength of the incisal part

By mixing the optimal amount of Tosoh Corporation’s new raw material “Zpex Smile.mⓇ”, high strength (1,100 MPa) is achieved uniformly in all layers while achieving gradations with excellent aesthetics. High transparency and high strength of the incisal edge are achieved.

Since the strength is same at any position on the disc, dental restorations can be placed according to the translucency required in each case. A single disc can be used for a wide range of cases; from inlays, onlays, laminate veneers and 14-tooth full bridges which require high strength.

Transition of translucency from the incisal area to the cervical area

The incisal part is designed to be highly translucent and the cervical part is designed to be low translucency, making it less affected by the color tone of the abutment tooth material or resin cement

Low deformation (warpage)

Thanks to optimize the ratio of zirconia powder, molding pressure, and presintering temperature, “warpage” is technically controlled, resulting in a good fit.

Chipping is less likely to occur

The disc is designed as high strength at all positions within the disc, and is easy to proceed with the milling process. It can be used safely in thin areas that are prone to chipping, such as at the incisal part, or in inlay cases where there is a margin around the entire circumference.